Water based ceramic non-stick coating C-106 is two layer ceramic coating, smooth hand feeling, excellent surface performance and chemical resistance. Superior initial non-stick property, easy to clean. It's ideal for internal coating and external coating of frying pan, stock pot, baking tray, electric fry pan and inner pot of electric cooker etc.
Ceramic nano material
PFOA free and excellent heat resistant
Excellent and lasting non-stick performance, easy to clean
Excellent chemical resistance, corrosion resistance and abrasive resistance
Appearance: White liquid (Primer and top)
Solid content (%): 35±1
Viscosity (cp): 600~900 Primer
Density (g/ml): 1.20 Primer/1.30 Top
pH: 8-11(Primer and top)
Color of the film surface: White (Flat and smooth)
Curing temperature (ºC): 280-300
Gloss (60° glossimeter): 10-20
Film thickness (μm): 30-45
Non-stick performance: >8 cycles (Fry eggs at 170±10ºC)
Corrosion resistance: No blister (Boling 10% salt water for 24 hours)
Abrasion resistance 3KG/21cm2: >4000 cycles
Hardness: >F (ZHONGHUA pencil)
-Cookware and bakeware made of aluminum, stainless and carbon steel etc.
Storage and handling
Available in 20 kg/ barrel or 30 kg/ barrel
Store products in tightly closed original containers at 5-40ºC
Shelf life: 9 months from delivery date
According to non-dangerous goods transport
HOW TO USE
1. Requirement on pre-treatment
-Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60ºC) for more than 6 minutes, dry it after water rinsing;
-Blast with 80#~120# corundum to make the surface roughness reach 2.0μ~3.0μ, pay attention to sandblast evenly;
-Wash with 1%~3% NaOH solution(60ºC) for more than 6 minutes, rinse with water;
-Wash with 1%~3% hydrochloric acid solution (60ºC) for more than 6 minutes, rinse with water and dry.
2. Preparation of the coating
-Dispersion of coating: the coating must be fully dispersed before operation;
-Viscosity adjustment: the viscosity could be adjusted according to different spray methods. Dilute with clean water if the viscosity is over high;
-Coating filtration: filtrate the coating with screen (100mesh) before using.
-The spraying environment should be dry, well-ventilated, no smoking and fire. We suggest using dedicated spray gun, elevated tank and curing oven;
-The air compressor should be degreased, dewatered and equipped with water oil separator before using;
-Roll the coating at 30rpm speed before using to make sure there is no sediment, and filter with 100 mesh screen;
-Adjust atomization and oil pump capacity of the spraying gun; make sure the unit is clean and flat;
-Preheat the substrate to 35ºC and spray the primer. Dry it at temperature of 120ºC~150ºC for 10min-15min. Keep the thickness of primer within 15μm-22μm;
-Spray top coating after the primer is dry and cooling to room temperature, then spray the top. Dry the unit at the temperature of 100ºC~150ºC for 10min, and gradually increase the temperature to 280ºC~300ºC. Keep for 10 min. Keep the thickness of top coat within 12μm~20μm. The thickness of two coat tally should be between 30μm~40μm;
-The oven (or the tunnel drier) must be well ventilated; otherwise, it will lead to color change of coating.