Non Stick Paint, Best Cookware Material, Non Stick Surface manufacturer / supplier in China, offering Water Based Fluororesin Primer and Top Coating, Super Hydrophobic Coating for Car Body, Water Based Polyurethane Sealer (SA-902) and so on.

(/ )

Supplier Homepage Product Fluoro Chemicals Non Stick Coating Water Based Fluororesin Primer and Top Coating

Water Based Fluororesin Primer and Top Coating

FOB Price: US $7.3-13.9 / kg
Min. Order: 1 kg
Min. Order FOB Price
1 kg US $7.3-13.9/ kg
Get Latest Price
Port: Shanghai, China
Production Capacity: 180tons/Month
Payment Terms: L/C, T/T, D/P, Western Union, Paypal, Money Gram, D/A

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: PF-600/B
  • Color: Black
  • Method: Spray
  • Main Raw Material: Water Based Fluororesin
  • Substrate: Iron
  • Packaging: Plastic Drum
  • Density (G/Ml): 1.20 Primer/1.30 Top
  • Color of The Film Surface: Black with Metallic (Flat and Smooth)
  • Gloss (60° Glossimeter): 10-20
  • Non-Stick Performance: >10 Cycles (Fry Eggs at 170degree Centigrade)
  • Trademark: SINOGRACE
  • Specification: Available in 20 kg/ barrel or 30 kg/ barrel
  • HS Code: 3824909990
  • Usage: Water Based Fluororesin
  • Appearance: Liquid
  • Components: Water Based Fluororesin
  • Certification: SGS
  • Expiration Date: 9 Months
  • Solid Content (%): 35
  • pH: 8-11 (Primer and Top)
  • Curing Temperature (ºC): 380-420
  • Film Thickness (μm): 20-30
  • Corrosion Resistance: No Blister
  • Transport Package: Available in 20 Kg/ Barrel or 30 Kg/ Barrel
  • Origin: China Anhui
Product Description

Description
Water based fluororesin non-stick coating PF-600 is designed with two-layer coating system. Thanks to its high density, good inadhesion, easy-to-clean performance and strong practicability. It is applicable for substrates like aluminum, alloy and stainless steel etc. 

Type
Water based fluororesin

Key features
Eco-friendly
Excellent heat resistant
Excellent chemical resistance and abrasive resistance
Excellent and lasting non-stick performance, easy to clean


Typical properties
Appearance:                                   Black liquid (Primer and top)
Solid content (%):                           35±1
Viscosity (cp):                                  600~1000 Primer
                                                        400~800 Top
Density (g/ml):                                 1.20 Primer/1.30 Top
pH:                                                   8-11 (Primer and top)
Color of the film surface:                  Black with metallic (Flat and smooth)
Curing temperature (ºC):                  380-420
Gloss (60° glossimeter):                  10-20
Film thickness (μm):                         20-30
Non-stick performance:                    >10 cycles (Fry eggs at 170±10ºC)
Corrosion resistance:                       No blister (Boling 10% salt water for 24 hours)
Abrasion resistance 3KG/21cm2:     >3000 cycles
Hardness (ZHONGHUA pencil):         >H


Application
-Aluminum, die-cast aluminum, alloy and stainless steel
-Frying pan, stock pot, baking tray, electric fry pan and inner pot of electric cooker etc.


Storage and handling
Available in 20 kg/ barrel or 30 kg/ barrel
Store products in tightly closed original containers at 5-40ºC
Shelf life: 9 months from delivery date
According to non-dangerous goods transport


HOW TO USE
1. Requirement on pre-treatment
-Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60ºC) for more than 6 minutes, dry it after water rinsing;
-Blast with 80#~120# corundum to make the surface roughness reach 2.0μ~3.0μ, pay attention to sandblast evenly;
-Wash with 1%~3% NaOH solution(60ºC) for more than 6 minutes, rinse with water;
-Wash with 1%~3% hydrochloric acid solution (60ºC) for more than 6 minutes, rinse with water and dry.

2. Preparation of the coating
-Dispersion of coating: the coating must be fully dispersed before operation;
-Viscosity adjustment: the viscosity could be adjusted according to different spray methods. Dilute with clean water if the viscosity is over high;
-Coating filtration: filtrate the coating with screen (100mesh) before using.

3. Application
-The spraying environment should be dry, well-ventilated, no smoking and fire. We suggest using dedicated spray gun, elevated tank and curing oven;
-The air compressor should be degreased, dewatered and equipped with water oil separator before using;
-Roll the coating at 30rpm speed before using to make sure there is no sediment, and filter with 100 mesh screen;
-Adjust atomization and oil pump capacity of the spraying gun; make sure the unit is clean and flat;
-Preheat the substrate to 35ºC and spray the primer. Dry it at temperature of 120ºC~150ºC for 10min-15min. Keep the thickness of primer within 12μm-18μm;
-Spray top coating after the primer is dry and cooling to room temperature, then spray the top. Dry the unit at the temperature of 100ºC~150ºC for 10~20 min, and gradually increase the temperature to 380ºC~420ºC. Keep for 10 min. Keep the thickness of top coat within 10μm~12μm. The thickness of two coat tally should be between 20μm~30μm;
-The oven (or the tunnel drier) must be well ventilated; otherwise, it will lead to color change of coating.

Water Based Fluororesin Primer and Top Coating
Water Based Fluororesin Primer and Top Coating
Water Based Fluororesin Primer and Top Coating
Water Based Fluororesin Primer and Top Coating

 

Send your message to this supplier
Avatar
Mr. Jack Tao
Manager
*From:
To: Mr. Jack Tao
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category