Two-Layer Nonstick Fluororesin Coating

FOB Price: US $7.6-13.6 / kg
Min. Order: 1 kg
Min. Order FOB Price
1 kg US $7.6-13.6/ kg
Get Latest Price
Port: Shanghai, China
Production Capacity: 300tons/Month
Payment Terms: L/C, T/T, D/P, Western Union, Paypal, Money Gram, D/A

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: PF-600/C
  • Color: Black
  • Method: Spray
  • Main Raw Material: Water Based Fluororesin
  • Substrate: Iron
  • Packaging: Plastic Drum
  • Density (G/Ml): 1.20 Primer/1.30 Top
  • Color of The Film Surface: Black with Metallic (Flat and Smooth)
  • Gloss (60° Glossimeter): 10-20
  • Non-Stick Performance: >10 Cycles (Fry Eggs at 170degree Centigrade)
  • Trademark: SINOGRACE
  • Specification: Available in 20 kg/ barrel or 30 kg/ barrel
  • HS Code: 3824909990
  • Usage: Water Based Fluororesin
  • Appearance: Liquid
  • Components: Water Based Fluororesin
  • Certification: SGS
  • Expiration Date: 9 Months
  • Solid Content (%): 35
  • pH: 8-11 (Primer and Top)
  • Curing Temperature (ºC): 380-420
  • Film Thickness (μm): 20-30
  • Corrosion Resistance: No Blister
  • Transport Package: Available in 20 Kg/ Barrel or 30 Kg/ Barrel
  • Origin: China Anhui
Product Description
DescriptionPF-600 is designed with two-layer coating system. Thanks to its high density, good inadhesion, easy-to-clean performance and strong practicability. It is applicable for substrates like aluminum, alloy and stainless steel etc.
TypeWater based fluororesin
Key featuresEco-friendly
Excellent heat resistant
Excellent chemical resistance and abrasive resistance
Excellent and lasting non-stick performance, easy to clean
Typical properties
AppearanceBlack liquid (Primer and top)
Solid content (%)35±1
Viscosity (cp)600~1000 Primer
400~800 Top
Density (g/ml)1.20 Primer/1.30 Top
pH8-11(Primer and top)
Color of the film surfaceBlack with metallic
(Flat and smooth)
Curing temperature (ºC)380-420
Gloss (60° glossimeter)10-20
Film thickness (μm)20-30
Non-stick performance
Fry eggs at 170±10ºC
>10 cycles
Corrosion resistance
Boling 10% salt water for 24 hours
No blister
Abrasion resistance 3KG/21cm2>3000 cycles
Hardness (ZHONGHUA pencil)>H
ApplicationAluminum, die-cast aluminum, alloy and stainless steel
Frying pan, stock pot, baking tray, electric fry pan and inner pot of electric cooker etc.
Storage and handlingAvailable in 20 kg/ barrel or 30 kg/ barrel
Store products in tightly closed original containers at 5-40ºC
Shelf life: 9 months from delivery date
According to non-dangerous goods transport
How to useRequirement on pre-treatment
Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60ºC) for more than 6 minutes, dry it after water rinsing;
Blast with 80#~120# corundum to make the surface roughness reach 2.0μ~3.0μ, pay attention to sandblast evenly;
Wash with 1%~3% NaOH solution(60ºC) for more than 6 minutes, rinse with water;
Wash with 1%~3% hydrochloric acid solution (60ºC) for more than 6 minutes, rinse with water and dry.
Preparation of the coating
Dispersion of coating: the coating must be fully dispersed before operation;
Viscosity adjustment: the viscosity could be adjusted according to different spray methods. Dilute with clean water if the viscosity is over high;
Coating filtration: filtrate the coating with screen (100mesh) before using.
The spraying environment should be dry, well-ventilated, no smoking and fire. We suggest using dedicated spray gun, elevated tank and curing oven;
The air compressor should be degreased, dewatered and equipped with water oil separator before using;
Roll the coating at 30rpm speed before using to make sure there is no sediment, and filter with 100 mesh screen;
Adjust atomization and oil pump capacity of the spraying gun; make sure the unit is clean and flat;
Preheat the substrate to 35ºC and spray the primer. Dry it at temperature of 120ºC~150ºC for 10min-15min. Keep the thickness of primer within 12μm-18μm;
Spray top coating after the primer is dry and cooling to room temperature, then spray the top. Dry the unit at the temperature of 100ºC~150ºC for 10~20 min, and gradually increase the temperature to 380ºC~420ºC. Keep for 10 min. Keep the thickness of top coat within 10μm~12μm. The thickness of two coat tally should be between 20μm~30μm;
The oven (or the tunnel drier) must be well ventilated; otherwise, it will lead to color change of coating.