WF-700 JS cement waterproof emulsion
| Description | A Suitable for polymer cement waterproofing slurry and polymer cement waterproof sand |
| Type | self-crosslinking acrylate copolymer emulsion |
| Key Features | Self - crosslinking acrylic copolymer emulsion u excellent superhydrophobic properties paint film has good low temperature flexibility and tensile strength excellent alkali resistance and excellent adhesion with the grassroots level |
| Typical Properties | | Appearance | Milky white liquid | | pH | 7-9 | | Solid content | 55% | | Glass Transition Temperature | -20ºC | | Viscosity (25ºC) | 2500-4000cP | | Ionic | anion | | Tensile strength | >1.1 MPa | | MFFT | 0ºC | | Freeze-Thaw Resistance, 5 cycles | Pass |
|
| APPLICATION | BasecoatsHigh-flexibility tile adhesivesRigid and flexible waterproofing slurries for sealing in conjunction with tiles and protective surface coatingsAnticorrosion protectionAdditive for hydraulic binder systemsRoof coverings |
Storage and
Handling | Available in 200 kg/ barrel or 25 kg/ barrel Store products in tightly closed original containers at 5-40ºCShelf life: 9 months from delivery dateAccording to non-dangerous goods transport |
test results of polymer cement waterproof coating
| No. | Test item | Technical Data | Test result | Individual assessment |
| 1 | The tensile strength,Mpa ≥ | 1.0 | 1.76 | qualified |
| 2 | Elongation at break,% ≥ | 300 | 367 | qualified |
| 3 | Low temperature flexible | -10ºC,No crack | No crack | qualified |
| 4 | Watertightness,0.3MPa,30min | waterproof | waterproof | qualified |
| 5 | Solid content,% ≥ | 65 | 70 | qualified |
| 6 | Dry time | Surface drying time ≤ | 4h | 2h | qualified |
| Full Drying Time ≤ | 8h | 4h | qualified |
| 7 | Tensile strength retention after processing,% | Heat treatment ≥ | 80 | 153 | qualified |
| Alkali treatment ≥ | 60 | 68 | qualified |
| Acid treatment ≥ | 40 | 62 | qualified |
| 8 | Tensile rate after treatment,% | Heat treatment ≥ | 200 | 285 | qualified |
| Alkali treatment ≥ | 520 | qualified |
| Acid treatment ≥ | 260 | qualified |
Note: The above experimental data objective and true, but not as a basis for reference, application methods and performance testing to your customer final assessment shall prevail. |